丙烯酸酯類單體
| 品名 Articles | 化學名稱 Chemical Name | 化學結構 Chemical formula | CAS No. | 玻璃轉移溫度 Tg(℃) | 表面張力 Surface Tension (dyne / cm) | 官能度 Functionality | 折射率 RI(at 25℃) | 分子量 Mw(g/mol) | 酸價(mgKOH/g) Acid Value | MEHQ含量 MEHQ(ppm) | 色度 Color(APHA) | 黏度(cps/25℃) Viscosity | 水份(ppm) Moisture | 比重(at 25℃) Sp.Gravility | 特性 Performance |
| UM81-010 | Ortho-Phenyl Phenoxy Ethyl Acrylate (OPPEA) | 91442-24-9 | 33 | 42 | 1 | 1.5750 | 268 | ≦0.2 | 100-500 | ≦50 | 120-160 | ≦700 | 1.11-1.16 | •高折射率 (High refractive index) •低收縮 (Low shrinkage) | |
| UM81-020 | 2-Phenoxy Ethyl Acrylate (PHEA) | 48145-04-6 | 7 | 40.1 | 1 | 1.5150 | 192 | ≦0.5 | 100-500 | ≦30 | 3-20 | ≦400 | 1.09-1.12 | •高反應性 (High reactivity) •低收縮 (Low shrinkage) •稀釋性佳 (Good dilution) | |
| UM81-070 | Lauryl acrylate (LA) | 2156-97-0 | - | 29 | 1 | 1.4420 | 240 | ≦0.5 | 100-500 | ≦30 | 4~8 | ≦1,000 | 1.42~1.47 | •低收縮 (Low shrinkage) •柔韌性佳 (Good flexbility) •耐水性佳 (Good water resistance) •耐候性佳 (Good weather resistance) | |
| UM81-080 | Stearyl Acrylate (SA) | 4813-57-4 | 46 | - | 1 | - | 324 | ≦0.5 | 150-250 | ≦100 | 10-20 (30℃) | ≦2,000 | 0.86-0.88 (30℃) | •低收縮 (Low shrinkage) •柔韌性佳 (Good flexbility) •耐水性佳 (Good water resistance) •耐候性佳 (Good weather resistance) | |
| UM82-010 | Dipropylene Glycol Diacrylate (DPGDA) | 57472-68-1 | 102 | 33.5 | 2 | 1.4500 | 242 | ≦0.5 | 400-800 | ≦60 | 6-14 | ≦2,000 | 1.03-1.11 | •低揮發性 (Low volatility) •低黏度 (Low viscosity) •稀釋性佳 (Good dilution) | |
| UM82-020 | Tripropylene Glycol Diacrylate (TPGDA) | 42978-66-5 | 62 | 33.3 | 2 | 1.4485 | 300 | ≦0.5 | 100-500 | ≦50 | 8-16 | ≦2,000 | 1.02-1.06 | •低揮發性 (Low volatility) •低黏度 (Low viscosity) •稀釋性佳 (Good dilution) | |
| UM82-030 | 1,6-Hexanediol Diacrylate (HDDA) | 13048-33-4 | 43 | 35.9 | 2 | 1.4560 | 226 | ≦0.3 | 100-500 | ≦30 | 5-10 | ≦400 | 1.00-1.04 | •低黏度 (Low viscosity) •稀釋性佳 (Good dilution) | |
| UM82-050 | Polyethylene Glycol (200) Diacrylate (PEG200DA) | 26570-48-9 | 14 | 40.1 | 2 | 1.463 | 308 | ≦0.5 | 200-1000 | ≦100 | 10-30 | ≦2,000 | 1.08-1.13 | •柔韌性佳 (Good flexbility) •低皮膚刺激性 (Low skin irritation) | |
| UM82-070 | Polyethylene Glycol (400) Diacrylate (PEG400DA) | 26570-48-9 | -25 | 42.6 | 2 | 1.4670 | 508 | ≦0.5 | 200-1000 | ≦100 | 30-70 | ≦2,000 | 1.11-1.12 | •柔韌性佳 (Good flexbility) •低皮膚刺激性 (Low skin irritation) | |
| UM82-080 | Polyethylene Glycol (600) Diacrylate (PEG600DA) | 26570-48-9 | -41 | 42.3 | 2 | 1.469 | 708 | ≦0.5 | 200-1000 | ≦100 | 80-120 | ≦2,000 | 1.11-1.14 | •柔韌性佳 (Good flexbility) •低皮膚刺激性 (Low skin irritation) | |
| UM82-105 | Ethoxylated Bisphenol-A Diacrylate (BPA10EODA) | 64401-02-1 | -7 | 44 | 2 | 1.5160 | 776 | ≦0.1 | 100-300 | ≦50 | 350-800 | ≦1,000 | 1.12-1.16 | •低氣味 (Low odor) •兼具親疏水平衡性 (Excellent hydrophilic/hydrophobic properties) •低皮膚刺激性 (Low skin irritation) •柔韌性佳 (Good flexbility) | |
| UM82-130 | Diethylene Glycol Diacrylate (DEGDA) | 4074-88-8 | - | - | 2 | 1.4590 | 214 | ≦0.5 | 200~1,000 | ≦50 | 5~15 | ≦1,000 | 1.08~1.12 | •低黏度 (Low viscosity) •稀釋性佳 (Good dilution) •低揮發性 (Low volatility) | |
| UM82-191 | Ethoxylated Bisphenol-A Diacrylate (BPA3EODA) | 64401-02-1 | 67 | 43.6 | 2 | 1.5450 | 468 | ≦0.1 | 100-300 | ≦50 | 1,200-1,800 | ≦1,000 | 1.14-1.15 | •高折射率 (High refractive index) •低氣味 (Low odor) •硬度佳 (Good hardness) | |
| UM82-211 | Ethoxylated 2-Methyl-1,3-Propanediol Diacrylate (MPD2EODA) | 634592-28-2 | - | 35 | 2 | 1.4570 | 286 | ≦0.5 | 300-500 | ≦100 | 13~20 | ≦1,000 | 1.05~1.07 | •低氣味 (Low odor) •低皮膚刺激性 (Low skin irritation) •柔韌性佳 (Good flexbility) | |
| UM82-240 | Bisphenol fluorene Diacrylate (OPPEA 40%) (BPEFDA) | 161182-73-6 91442-24-9 | - | - | 2 | 1.600 | 546 | ≦0.3 | 800-1,300 | ≦40 | 15,000-30,000 | ≦1,000 | - | •高折射率 (High refractive index) •高光澤 (High gloss) •硬度佳 (Good hardness) | |
| UM82-257 | Ethoxylated Bisphenol fluorene Diacrylate (BPEF15EODA) | 917867-33-5 | - | - | 2 | 1.5450 | 1121 | ≦0.3 | 500-1,000 | ≦50 | 3,400-4,200 | ≦2,000 | - | •高折射率 (High refractive index) •彈性佳 (Good elasticity) •硬度佳 (Good hardness) | |
| UM82-264 | Ethoxylated Bisphenol-A Diacrylate (BPA8EODA) | 64401-02-1 | - | 43 | 2 | 1.5230 | 685 | ≦0.1 | 100-300 | ≦50 | 600-900 | ≦1,000 | 1.11-1.15 | •低揮發性 (Low volatility) •硬度佳 (Good hardness) •附著力佳 (Good adhesion) •柔韌性佳 (Good flexbility) | |
| UM83-010 | Trimethylolpropane Triacrylate (TMPTA) | 15625-89-5 | 62 | 36.6 | 3 | 1.4720 | 296 | ≦0.3 | 100-500 | ≦50 | 80-120 | ≦1,000 | 1.08-1.13 | •固化速度快 (Fast cure speed) •高反應性與交聯密度 (High reactivity & High crosslink density) •硬度佳 (Good hardness) •耐磨性佳 (Good abrasion) | |
| UM83-021 | Ethoxylated Trimethylolpropane Triacrylate (TMP3EOTA) | 28961-43-5 | 40 | 36.1 | 3 | 1.4710 | 428 | ≦0.5 | 180-350 | ≦50 | 40-80 | ≦1,500 | 1.09-1.12 | •低黏度 (Low viscosity) •固化速度快 (Fast cure speed) •耐化性佳 (Good chemical resistance) | |
| UM83-030 | Pentaerythritol Triacrylate (PET3A) | 3524-68-3 | 42 | 40.6 | 3 | 1.4840 | 298 | ≦0.5 | - | ≦60 | 600-1,200 | ≦2,000 | 1.16-1.19 | •固化速度快 (Fast cure speed) •高交聯密度 (High crosslink density) •硬度佳 (Good hardness) •具可反應的羟基基團 (Containing hydroxy group to react) | |
| UM83-042 | Ethoxylated Trimethylolpropane Triacrylate (TMP6EOTA) | 28961-43-5 | -8 | 39.6 | 3 | 1.4690 | 560 | ≦0.1 | 100-300 | ≦50 | 80-120 | ≦1,500 | 1.09-1.12 | •柔韌性佳 (Good flexbility) •固化速度快 (Fast cure speed) •耐化性佳 (Good chemical resistance) | |
| UM84-021 | Ethoxylated pentaerythritol tetraacrylate | 51728-26-8 | 36 | - | 4 | 1.4750 | 571 | ≦0.5 | 200~600 | ≦100 | 120~200 | ≦1,000 | 1.12~1.16 | •高反應性與交聯密度 (High reactivity & High crosslink density) •耐化性佳 (Good chemical resistance) | |
| UM84-030 | Ditrimethylolpropane Tetraacrylate (DiTMP4A) | 94108-97-1 | 42 | 36 | 4 | 1.4760 | 466 | ≦0.5 | 400-600 | ≦100 | 600-900 | ≦1,000 | 1.05-1.15 | •固化速度快 (Fast cure speed) •高交聯密度 (High crosslink density) •硬度佳 (Good hardness) •具可反應的羟基基團 (Containing hydroxy group to react) | |
| UM86-010 | Dipentaerythritol Hexaacrylate (DPHA) | 29570-58-9 | 54 | 43 | 6 | 1.4890 | 579 | ≦0.5 | 400-600 | ≦50 | 4,000-7,000 | ≦1,000 | 1.17-1.19 | •高反應性與交聯密度 (High reactivity & High crosslink density) •固化速度快 (Fast cure speed) •附著力佳 (Good adhesion) |